PC-MBS Resin M-715
MBS 5% / PC 70% + ABS 25% |
Property | Test Standard | Test Condition | Unit | Value |
Mechanical Properties |
Tensile Strength at Yield | ASTM D-638 | 50 mm/min | MPa | 65 |
Elongation at Break | ASTM D-638 | 50 mm/min | % | 70 |
Flexural Strength at Yield | ASTM D-790 | 10 mm/min | MPa | 85 |
Flexural Modulus | ASTM D-790 | 10 mm/min | MPa | 2,400 |
Rockwell Hardness | ASTM D-785 | 23℃, 750 g | RH | 112 |
Notched Izod Impact Strength | ASTM D-256 | 3.2 mm, 23℃ | kJ/m² | 60 |
Physical Properties |
Melt Flow Rate | ASTM D-1238 | 260℃, 5 kg | g/10 min | 25 |
Density | ASTM D-792 | 23℃ | g/cm³ | 1.13 |
Thermal Properties |
Heat Deflection Temperature | ASTM D648 | 0.45 MPa | ℃ | - |
ASTM D648 | 1.80 MPa | ℃ | 112 |
Application Areas
Used to improve the impact strength and compatibility of PC, PBT, PET, ABS, PC/PBT alloys, and PC/ABS alloys.
Product Characteristics
Methyl Methacrylate-Butadiene-Styrene (MBS) is a white, odorless powder with high strength and rigidity. It maintains sufficient rigidity at temperatures of 85–90℃.
It offers excellent low-temperature performance and maintains good toughness at -40℃. With excellent transparency and light transmittance of up to 80%–90%, it also provides good oil resistance and resistance to weak acids and alkalis. Its outstanding transparency and UV aging resistance are among its key advantages.
MBS is also an excellent polymer modifier that improves the transparency and impact resistance of polymer materials.