PC-MBS Resin M-725
MBS 5% / PC 70% + ABS 25% |
Property | Test Standard | Test Condition | Unit | Value |
Mechanical Properties |
Tensile Strength at Yield | ASTM D-638 | 50 mm/min | MPa | 67 |
Elongation at Break | ASTM D-638 | 50 mm/min | % | 85 |
Flexural Strength at Yield | ASTM D-790 | 10 mm/min | MPa | 87 |
Flexural Modulus | ASTM D-790 | 10 mm/min | MPa | 2,450 |
Rockwell Hardness | ASTM D-785 | 23℃, 750 g | RH | 112 |
Notched Izod Impact Strength | ASTM D-256 | 3.2 mm, 23℃ | kJ/m² | 68 |
Physical Properties |
Melt Flow Rate | ASTM D-1238 | 260℃, 5 kg | g/10 min | 20 |
Density | ASTM D-792 | 23℃ | g/cm³ | 1.13 |
Thermal Properties |
Heat Deflection Temperature | ASTM D648 | 0.45 MPa | ℃ | - |
ASTM D648 | 1.80 MPa | ℃ | 112 |
Application Areas
Used to improve the impact resistance and compatibility of PC, PBT, PET, ABS, PC/PBT alloys, and PC/ABS alloys.
Comparable Manufacturers and Products
USA: Rohm and Haas
Japan: Kaneka
Metablen C Series
Japan: Mitsubishi Chemical
South Korea: LG Chem
Atofina
Product Characteristics
Methyl Methacrylate-Butadiene-Styrene (MBS) is a white, odorless powder with high strength.
It offers excellent rigidity and can maintain sufficient stiffness at temperatures of 85–90℃.
It provides excellent low-temperature performance and maintains good toughness even at -40℃.
It features excellent transparency, with light transmittance of up to 80%–90%, as well as good oil resistance and resistance to weak acids and alkalis. Its transparency and UV aging resistance are among its outstanding advantages.
MBS is also an excellent polymer modifier that improves the transparency and impact resistance of polymer materials.